Semiconductor device manufacturing method and semiconductor device

ABSTRACT

A semiconductor device manufacturing method comprises a step of forming a trench to a first insulation film formed on a semiconductor substrate, and forming a lower level wiring in the trench, a step of forming at least one conductive layer on the semiconductor substrate to coat the lower level wiring, a step of forming at least one thin film layer on the conductive layer, a step of forming a hard mask by patterning the thin film, a step of etching the conductive layer by using the hard mask as an etching mask, and forming a conductive pillar-shaped structure, whose upper surface is covered with the hard mask, on the lower level wiring, a step of forming a second insulation film on the semiconductor substrate so that the pillar-shaped structure is buried, a step of forming a wiring trench in which at least the hard mask is exposed, and a step of burying a conductor into the wiring trench after the hard mask is removed, and forming an upper level wiring in the wiring trench.

BACKGROUND OF THE INVENTION

The present invention relates to a semiconductor device of multi-levelwiring structure such as a logic LSI (Logical Large Scale IntegratedCircuit), a DRAM (Dynamic Random Access Memory), SRAM (Static RAM), aCMOS (Complementary Metal Oxide Semiconductor) or a bipolar transistor(Bipolar Transistor), especially, to a formation of multi-level wiringwhich includes via-contact formation using wiring formation and aconductive pillar-shaped structure (pillar), and a semiconductor devicewhich has a multi-level wiring structure.

Conventionally, in general, when a connection plug, which electricallyconnects between the wirings of the upper level and the lower level inthe multi-level wiring structure of the semiconductor device, is formed,a method of opening a contact hole by using a reactive ion etching (RIE(Reactive Ion Etching)) method etc. for an interlevel insulation film,and forming the connection plug by burying a conductive material such asmetal is used.

This conventional art has the following disadvantages. At the RIE forthe opening of the contact hole, physical damage and corrosion arecaused on the surface of lower level wiring exposed to the bottom of thecontact hole with the etching gas and the sputtered particle. A contactresistance between the above-mentioned connection plug and the lowerlevel wiring rises by adhering the etching residue and the sputteredparticle. When the contact hole is not formed at a desired position bythe occurrence of the missalignment with the lower wiring pattern atformation of the contact hole, the lower wiring side and the interlevelinsulation film thereunder are excessively etched by RIE. In addition,the undesirable short-circuit with the wiring of the lower level isoccurs, and the cave remains around a fine wiring. As a result, thereliability lowers.

When the lower level wiring is formed, a method of forming a conductivepillar-shaped structure (pillar) and the lower level wiring at the sametime is known. This method is a method of depositing a metal film on theinsulation film formed on the semiconductor substrate, forming theconnection plug with a photo-lithography and the etching methods such asan RIE and leaving a metal film in the trench to form the lower levelwiring. However, the lower level wiring is the same material as theconnection plug, and changing both of the material cannot broaden thevariety of the selection of the material. Moreover, when the connectionplug is etched, the lower level wiring might be over-etched. Inaddition, the missalignment might be occurred when the connection plugand the upper level wiring are connected.

Recently a high speed operation has come to be requested to the device.Therefore, a lower resistance material is required as for the wiringmaterial. Copper (Cu) has been paid attention so as to respond to therequest and is multi-used. The electrical resistivity of the copper is1.8 μΩcm, and it is greatly low among the wiring material. Besides this,tungsten (W) whose resistivity is 10 to 20 μΩcm and aluminum (Al) whoseresistivity is 3 to 4 μΩcm are used well as a wiring material.Therefore, AlCu alloy is used as any of the lower level wiring 12, theconnection plug 14 (conductor pillar), and the upper level wiring 18shown in FIG. 1A and FIG. 1B, for example, but is considered that thewiring resistance is reduced by using Cu for the lower level wiring 12and the upper level 18, and using Al for the connection plug 14.

However, the.inconvenience might happen when Cu is used as it is. First,Cu has characteristics to diffuse into the insulation film in the stateof the atom when Cu is covered by the insulation film. Especially, themoving of Cu becomes active if Cu is heated by the use of the device andthe heat-treating step under manufacturing, then the wiring is destroyedand comes to cause the disconnection and the short-circuit accidenteasily. Moreover, the surface is oxidized when Cu is exposed in (the)air, and advantage of the low resistance is lost.

Moreover, in the above-mentioned pillar technology, since thepillar-shaped structure (pillar) is formed only to connection part ofthe lower level wiring and the upper level wiring, the ratio of theregion where the pillar-shaped structure is formed becomes very smalland is about several % or less of the whole. Therefore, thepillar-shaped structure is excessively etched, for example, when thedrying etching, and the processing of the pillar-shaped structurebecomes difficult. The planarity of the interlevel insulation filmformed after processing of the pillar-shaped structure deteriorates.

As described above, since the ratio of the region where thepillar-shaped structure is formed is very small when the pillartechnology is used for the connection of the lower level wiring and theupper level wiring, there is a subject matter of a bad processingcontrol of the pillar-shaped structure and a bad planarity of theinterlevel insulation film.

BRIEF SUMMARY OF THE INVENTION

An object of the present invention is as follows.

(1) To provide a semiconductor device manufacturing method having themulti-level wiring structure which can secure the space, in which thecontact structure between the lower level wiring and the upper levelwiring is arranged, before depositing the interlevel insulation film,can prevent from the damage at RIE and impurities on the surface ofwiring under the contact hole, and can secure the reliability with thecontact of the lower level wiring even if the missalignment is occurredat the contact hole.

(2) To provide a semiconductor device manufacturing method which has themulti-level wiring structure to connect between wirings in which theprotection film to control the diffusion of the wiring material into theinsulation film (or, to control the oxidation of the wiring material)can be deposited without greatly increasing steps, and the semiconductordevice manufactured by the method.

(3) To provide a manufacturing method capable of improving theprocessing controllability and the planarity of the interlevelinsulation film of the pillar-shaped structure (pillar) when the pillartechnology is used to connection step of the lower level wiring and theupper level wiring.

According to the first aspect of the present invention, in thesemiconductor device manufacturing method or the semiconductor device, ahard mask is formed on upper portion of the pillar, the process isadvanced with leaving the hard mask, and the hard mask is removedimmediately before connecting the pillar with the upper level wiring,when the lower level wiring (the first buried wiring) and the upperlevel wiring (the second wiring) are connected with the pillar-shapedstructure (pillar). Where, it is desirable to form a protection film onthe surface of the lower level wiring uncovered with at least thepillar-shaped structure after the pillar-shaped structure is formed.

The hard mask may be a silicon oxide, a silicon nitride, or a tungsten.

The first aspect of the present invention comprises the followingfeatures. First, after the first buried wiring (lower level wiring)which consists of Cu is formed on the first interlevel insulation film,a conductive layer, in which the connection plug which consists of, forexample, Al/W/WN or Cu, etc. is formed, is formed. Next, this conductivelayer is processed to the connection plug by the lithography technologyand the RIE method. That is, in the first aspect of the presentinvention, a hard mask materials such as the silicon nitride film or thesilicon oxide film for forming the connection plug is deposited as anetching mask on a conductive layer where the connection plug is formed.The protection film such as silicon nitride films (Si₃N₄) with an effectby which the diffusion of Cu to the interlevel insulation film iscontrolled and an effect by which the oxidation of the Cu surface iscontrolled is deposited on the connection plug and the first interlevelinsulation film by the CVD method or the reactive sputtering method,etc. as desired thickness if necessary. Thereafter, the secondinterlevel insulation film is deposited, the upper level wiring isburied in the second interlevel insulation film. As a result, the lowerlevel wiring and the upper level wiring are connected by the connectionplug.

In addition, since the protection film which has a Cu diffusionprevention effect and an oxidation control effect in the region wherethe connection plug on the first buried wiring (lower level wiring) doesnot exist is deposited, and neither the first buried wiring (lower levelwiring) nor the interlevel insulation film are not contacted directlyunlike the conventional ones, an excellent characteristic is obtainedwithout requiring the complicated steps. Both of the hard mask and theprotection film also have an advantage of enlarging the differenceallowance in the depth direction when the second wiring trench isprocessed.

Therefore, the difference allowance in the depth direction is enlarged,and the poor coverage of the barrier metal of the upper level isprevented by the present invention. In addition, the Cu diffusion fromthe lower level wiring can be prevented according to the presentinvention.

The upper surface of the pillar to take the electric contact with thewiring can be prevented from oxidizing during the process, beingpolluted, and occurring the chemical reaction by leaving a hard maskuntil the formation of the second wiring trench.

In the second aspect of the present invention, a semiconductor devicecomprises: a semiconductor substrate in which a first insulation layerhaving a trench where a lower level wiring is buried is formed; aconductive layer having a component which includes a barrier metalfunction formed on the lower level wiring; a conductive pillar-shapedstructure which is connected with the conductive layer and is formed onthe semiconductor substrate; and a second insulation layer formed on thesemiconductor substrate in order to surround the pillar-shapedstructure, and the second insulation layer has a trench formed to exposean upper portion of the pillar-shaped structure. And, an upper levelwiring which is electrically connected with the pillar-shaped structureis formed in the trench.

The preferred manner of the second aspect is as follows.

(1) The conductive layer has at least two layers. Or, the conductivelayer includes WN, and, desirably, the conductive layer further includesW. The connection plug on the first buried wiring (lower level wiring)has, for example, Al which is a main material of the connection plug anda conductive layer to prevent from over-etching to the first buriedwiring when the Al is processed to the pillar-shaped structure by theRIE processing. In addition, when each material of the first buriedwiring and the connection plug is different, for example, Cu as thewiring material and Al as the plug material. For example, WN can beapplied as a conductive layer to meet this requirement, but since the WNhas a high resistivity, the WN raises the entire resistance of theconnection plug when a necessary film thickness is formed to have enoughstopper function. Therefore, preferably, W which has only the stopperfunction and the electrical resistivity thereof is small is stackedthereto. As a result, the connection plug having the stopper functionand the barrier function as W and WN stacking film, and low resistancecan be formed. That is, the above-mentioned advantage is achieved bywhich the conductive layer has at least first and second layers, thefirst layer of the conductive layer functions as an etching stopper anda barrier layer when the pillar-shaped structure is processed, and thesecond layer of the conductive layer has a lower resistance than thefirst layer of the conductive layer, and functions as an etching stopperwhen the pillar-shaped structure is processed.

(2) The surface of the lower level wiring and the first insulation layeris substantially in the same plane, the conductive layer is formed so asto be connected with at least a part of the lower level wiring, and thesemiconductor device further comprises a protection film covering thesurface of the lower level wiring which is uncovered with thepillar-shaped structure and formed to be deposited on an upper portionof the pillar-shaped structure. The allowance becomes large since theprotection film can be used as a position alignment allowance betweenthe second wiring trench bottom and the upper surface of the pillar inthe depth direction.

(3) The conductive layer is formed in the trench to cover all surfacesof the lower level wiring. Though the lower level wiring is covered withthe protection film for preventing the Cu diffusion in (2), there is anadvantage of reducing the capacity between the wirings since it isunnecessary to cover the upper surface of the wiring with the protectionfilm having high permittivity (for example, SiN).

(4) The conductive layer includes the material which can be selectivelyetched for the first insulation film. Where, a horizontal section of thepillar-shaped structure is narrower than a horizontal section of theconductive layer. The pillar-shaped structure or the conductive layerhas the shape of widening toward the end. The protection film formed tocover a sidewall of the pillar-shaped structure, the lower level wiring,and the first insulation layer is further provided.

(5) The pillar-shaped structure includes copper or an alloy thereof.

(6) The conductive layer is used as a CMP stopper when the lower levelwiring is formed by the CMP.

According to the second aspect of the present invention, the protectionfilm which has a Cu diffusion prevention effect and an oxidation controleffect is deposited in the region where the connection plug on the firstburied wiring (lower level wiring) does not exist, and since neither thefirst buried wiring (lower level wiring) nor the interlevel insulationfilm are not contacted directly unlike the conventional ones, anexcellent characteristic can be obtained without requiring thecomplicated steps. In addition, the protection film consisting of thesilicon nitride film deposited on the connection plug, also has the samefunction as the hard mask which enlarges the difference allowance in thedepth direction when the second wiring trench is processed.

Moreover, since the narrow space between connection plug and the side ofthe second wiring trench, which is formed when the position of thebottom of the upper level wiring is lower than an uppermost surface ofthe connection plug, is not made, a coverage degradation etc. of thebarrier metal of the upper level wiring in this part are prevented.

A part of the bottom of the connection plug shifts from the lower levelwiring because of miss alignment when the connection plug is formed onthe lower level wiring with borderless structure (without fringe at theconnection region for a alignment allowance). Then, over-hanging shapeis optionally provided under the connection plug by forming a conductivelayer, which has a broader horizontal section than the pillar-shapedstructure, on the first interlevel insulation film to surely achieve theprotection film formation on this part, and the protection film withhigh reliability which can surely cover and protect the connection plugis formed.

According to the present invention, in the multi-level wiring structureinterconnected by using a pillar-shaped connection plug, the formationof the protection film to which the entire pillar is covered becomespossible. The possibility of the metal material which can be selected asthe connection plug extends, and, for example, the material with anextremely low electrical resistivity like copper can be selected.

According to the third aspect of the present invention, a semiconductordevice comprises a plurality of pillar-shaped structures formed inconnection regions where a lower level wiring and an upper level wiringare electrically connected, a plurality of dummy pillar-shapedstructures formed in predetermined regions except the connectionregions, and an interlevel insulation film formed to cover the pluralityof pillar-shaped structures, wherein layout data of the dummypillar-shaped structures formed in the predetermined regions areobtained by a NOR processing of corresponding data to both informationwhich are based on a layout information of layout of the lower levelwiring and layout information of layout of the upper level wiring.Where, the pillar-shaped structures formed in the connection regions andthe predetermined regions are formed with the conductor.

Moreover, another semiconductor device according to the third aspect ofthe present invention comprises a plurality of pillar-shaped structuresformed in connection regions where a lower level wiring and an upperlevel wiring are electrically connected, a plurality of dummypillar-shaped structures formed in predetermined regions except theconnection regions, and an interlevel insulation film formed to coverthe plurality of pillar-shaped structures, wherein data of layout of thepillar-shaped structures formed in the predetermined regions is obtainedby a NOT processing of data corresponding to the information based onlayout information at the layout of the connection region.

The preferred manners of the third aspect of the present invention areas follows.

(1) The pillar-shaped structures formed in the connection regions areremoved, after the interlevel insulation film is formed.

(2) The dummy pillar-shaped structures formed in the connection regionand the predetermined regions are formed with an insulator.

(3) The dummy pillar-shaped structures formed in the predeterminedregions are formed in regions except the predetermined specific regions.

According to the third aspect of the invention, the pillar-shapedstructures (pillars) are formed in regions other than the connectionregions where the lower level wirings and the upper level wirings areelectrically connected. Therefore, the ratio of the regions where thepillar-shaped structures are formed can be greatly increased locallyand/or overall, the processing controllability of the pillar-shapedstructures, which is difficult in conventional ones, can be improved,and the planarity of the interlevel insulation film can be improved.

The layout of the pillar-shaped structures (dummy pillar-shapedstructures) formed in the predetermined regions except the connectionregions can be determined by the following arithmetic processing.

The method of the first arithmetic processing is a method of performinga NOR processing of data corresponding to both information which arebased on a layout information of layout of the lower level wiring and alayout information of layout of the upper level wiring. An OR processingof the data obtained by the above mentioned arithmetic processing withthe data corresponding to the connection region is preformed, and a maskto form the pillar-shaped structures based on the data obtained by theOR processing is manufactured. The mask pattern data, which correspondsto the dummy pillar-shaped structures, can be generated by performingthe processing divided the region corresponding to the data obtained forexample by the NOR processing into the plurality of island-shapedregions which are mutually separated.

The pillar-shaped structure is formed in the regions where neither thelower level wiring nor the upper level wiring are arranged besides theconnection region of the lower level wiring and the upper level wiringby the pattern transfer using the mask thus manufactured. Therefore, theratio of the region where the pillar-shaped structures are formed can beincreased locally and/or overall.

When the pillar-shaped structures are formed by using the maskmanufactured by the first arithmetic processing method, it is alsopossible to leave the pillar-shaped structures without removing afterthe interlevel insulation film is formed since the pillar-shapedstructures are not formed in the regions where the lower level wiringsand the upper level wirings are arranged. Therefore, the pillar-shapedstructures formed in the connection regions and the predeterminedregions except connection regions are formed with the conductor, and thepillar-shaped structures formed in connection regions can be used as theconnection material of the lower level wirings and the upper levelwirings.

The second arithmetic processing method is performing NOT processing ofdata corresponding to the information which is based on the layoutinformation of the layout of connection regions of the lower levelwiring and the upper level wiring. The OR processing of data obtained bythe above mentioned arithmetic processing and data corresponding toconnection regions is performed, and the mask to form the pillar-shapedstructures based on the data obtained by this OR processing ismanufactured. For example, the mask pattern data corresponding to thedummy pillar-shaped structures can be generated by performing theprocessing which divides the region corresponding to data obtained by aNOT processing into the plurality of island-shaped regions beingmutually separated.

The pillar-shaped structures can be formed in all regions exceptconnection regions of the lower level wiring and the upper level wiringby transferring the pattern using the mask manufactured described above.That is, it is different from the first arithmetic processing method,and it becomes possible to form the pillar-shaped structures in theregions where the lower level wirings and the upper level wirings arearranged. Therefore, the ratio of the region where the pillar-shapedstructures are formed can become larger than the first arithmeticprocessing method.

When the pillar-shaped structures are formed in the predeterminedregions except connection regions by the manufacturing method, forexample, the first arithmetic processing method or the second arithmeticprocessing method, the pillar-shaped structures in the predeterminedregions may be formed only in the regions except the predeterminedspecific regions (specific circuit region).

That is, when the layout of the pillar-shaped structures are determinedby the arithmetic processing, the dummy pattern of the pillar-shapedstructures is not generated for the predetermined specific region.Specifically, the dummy pattern is prevented from being generated for anundesirable specific regions, in which the dummy pillar-shapedstructures are formed, in the circuit performance and the chipcharacteristic.

For example, the following regions are given as specific regions wherethe dummy pattern is not generated. First, regions where the circuitinfluenced by the parasitic capacity caused by the interlevel insulationfilm is arranged can be given. Regions where the spare circuit section,the redundancy circuit section, and the fuse section arranged in thecircuit section are formed can be also given. In addition, regions wherethe terminal section (PAD section) for an external connection is formedand other regions where the dicing line section is provided can be givenas specific regions.

As described above, according to the present invention, thepillar-shaped structures are formed in regions other than connectionregions where the lower level wiring and the upper level wiring areelectrically connected. Therefore, the ratio of the region where thepillar-shaped structure is formed can be greatly increased locally andoverall, a processing controllability by pillar-shaped structure whichis difficult conventionally can be improved, and improving the planarityof the interlevel insulation film becomes possible.

Additional objects and advantages of the invention will be set forth inthe description which follows, and in part will be obvious from thedescription, or may be learned by practice of the invention. The objectsand advantages of the invention may be realized and obtained by means ofthe instrumentalities and combinations particularly pointed outhereinafter.

BRIEF DESCRIPTION OF THE SEVERAL VIEWS OF THE DRAWINGS

The accompanying drawings, which are incorporated in and constitute apart of the specification, illustrate presently preferred embodiments ofthe invention, and together with the general description given above andthe detailed description of the preferred embodiments given below, serveto explain the principles of the invention.

FIG. 1A and FIG. 1B are the conventional manufacturing step sectionalview and plan views of the semiconductor device;

FIG. 2A and FIG. 2B are the manufacturing step sectional view and planview of the semiconductor device according to the first embodiment;

FIG. 3A and FIG. 3B are the manufacturing step sectional view and planview of the semiconductor device according to the first embodiment;

FIG. 4A and FIG. 4B are the manufacturing step sectional view and planview of the semiconductor device according to the first embodiment;

FIG. 5A to FIG. 5J are the manufacturing step sectional views of thesemiconductor device according to the second embodiment of the presentinvention;

FIG. 6 is a plan view of the manufacturing step sectional vire of FIG.5J.

FIG. 7 shows another embodiment in the step of FIG. 5H;

FIG. 8A to FIG. 8D show the case that there is the missalignment on theupper interface in the second embodiment;

FIG. 9A to FIG. 9H (including FIG. 9F′ and FIG. 9G′) are manufacturingstep sectional views of the semiconductor device according to the thirdembodiment;

FIG. 10 shows another embodiment in the step of FIG. 9E;

FIG. 11A to FIG. 11C show the second modification of the thirdembodiment;

FIG. 12 is a sectional view of the semiconductor device which explainsthe fourth embodiment;

FIG. 13A to FIG. 13F are manufacturing step sectional views of thesemiconductor device according to the fourth embodiment;

FIG. 14A and FIG. 14B are the manufacturing step sectional views of thesemiconductor device according to the fifth embodiment;

FIG. 15 is a manufacturing step sectional view of the semiconductordevice according to the fifth embodiment;

FIG. 16A and FIG. 16B are the manufacturing step sectional views of thesemiconductor device according to the sixth embodiment;

FIG. 17A and FIG. 17B are the manufacturing step sectional views of thesemiconductor device according to the seventh embodiment;

FIG. 18 is a manufacturing step sectional view of the semiconductordevice according to the seventh embodiment;

FIG. 19A to FIG. 19C are step sectional views sequentially showing thesteps regarding to the manufacturing method according to the eighthembodiment of the present invention;

FIG. 20 shows the generation procedure of the mask data to form thepillar in the eighth embodiment of the present invention;

FIG. 21 shows the generation procedure of the mask data to form thepillar in the ninth embodiment of the present invention;

FIG. 22A to FIG. 22F are step sectional views sequentially showing thesteps regarding to the manufacturing method according to the ninthembodiment of the present invention;

FIG. 23 shows the generation procedure of the mask data to form thepillar in the tenth embodiment of the present invention;

FIG. 24 shows the generation procedure of the mask data to form thepillar in the tenth embodiment of the present invention; and

FIG. 25A to FIG. 25F are step sectional views sequentially showing thestep regarding to the manufacturing method according to the tenthembodiment of the present invention.

DETAILED DESCRIPTION OF THE INVENTION

Hereinafter, the embodiment of the invention will be explained referringto the drawings.

The first embodiment of the present invention will be explainedreferring to FIG. 2A to FIG. 4B.

The semiconductor device manufacturing method according to the presentinvention is applied to a step (Hereinafter, referred to as Damascenestep) of processing a trench-shaped or a hole-shaped trench to aninsulation film when the semiconductor device is manufactured, andforming a buried wiring therein by depositing a conductive material suchas the metals. Then, the pillar-shaped temporary connection plug(pillar-shaped structure: Pillar) is formed with an arbitrary materialin the part which becomes a connection plug when the connection wiring(Hereinafter, referred to as a “connection plug”), to which an upperlevel wiring and a lower level wiring are connected, is formed.Thereafter, an interlevel insulation film is deposited. When theconductor is used for the temporary connection plug material, it is leftas connection wiring. In a step of processing the trench for the upperlevel wiring and burying the wiring material or a step of replacing thepillar-shaped structure for the connection wiring material, thereplacing step is performed before or after processing the trench of theupper level wiring, and thereafter or simultaneously the wiring materialof the upper level wiring is buried.

It becomes possible to secure the space for arranging a contact betweenthe lower level wiring and the upper level wiring before depositing theinterlevel insulation film by using this method. It becomes possible toform the connection plug having the low resistance since opening step ofthe conventional contact hole, which has the problems such as the damageat RIE and lying impurities at the bottom of the hole, is unnecessary.In addition, the reliability of the contact with the lower level wiringcan be secured even if the missalignment is occurred at the step ofcontact plug formation. The size restriction to the connection plug canbe lost and the processing allowance can be enlarged by using the pillarstep, though by the similar reasons it is necessary to reduce thediameter of a contact hole more than the width of the lower levelwiring, in the conventional hole opening step. Here, “Allowance” is anallowance (permission) of the position alignment in the horizontaldirection of the wiring and the connection plug.

Hereafter, an example of the above-mentioned conventional art will beexplained referring to the drawings. In this example, a method offorming a connection plug by using a conductor pillar, and forming anupper level wiring connected to this connection plug will be described.FIG. 2A to FIG. 4B are manufacturing step sectional view and a plan viewof the semiconductor device according to the present invention. Thesemiconductor substrate 10 is shown in FIG. 2A and FIG. 4A, but isomitted in other Figures. For example, the silicon semiconductor is usedfor the semiconductor substrate 10.

A first insulation film 11, which consists of the silicon oxide filmetc. formed by the CVD (Chemical Vapor Deposition) method etc. on thesemiconductor substrate 10, is formed. The first insulation film 11 isplanarized, and the first wiring trench of the same shape as the wiringpattern of the lower level wiring is formed on the surface thereof. Themetal, which consists of, e.g., the AlCu alloy, is buried in the firstwiring trench, and the lower level wiring 12, which is the first wiring,is formed (FIG. 2A and FIG. 2B). Here, the aluminum alloy (AlSiCu), Cu,and W, etc. generally used as a wiring material for a material of thelower level wiring 12 may be used. Next, the AlCu metal layer is formedon the first insulation film 11 and the lower level wiring 12 by thesputtering method etc. Thereafter, the pattern of the pillar-shapedstructure 14 (Hereinafter, called as a pillar) is formed by etching theAlCu metal layer by the RIE method etc. Though AlCu is used here as apillar material, it is desirable the metal layer is the material whichcan be used as a fine metallic wiring and has a low resistivity, and,for example, Al, AlSiCu, and Cu, etc. can be used.

Next, a second insulation film 15, which consists of the silicon oxidefilm etc., is formed by either the CVD method or the spin coat method,etc. to bury the pattern of the conductor pillar 14 which consists ofthe metal layer. The step of forming the second insulation film 15 isdivided into several-steps and a step of reforming the insulation filmby performing heat-treating etc. may be added during the several-stepsfor the purpose to improve the planarity of the buried insulation filmand the purpose to improve the step coverage and the gas filling.Moreover, the stacking structure of several kinds of differentinsulation films can be used as the second insulation film 15. Inaddition, the planarizing step can be added by using a chemicalmechanical polishing (CMP) method or the resist etch-back method, etc.to decrease the roughness of the surface of the formed second insulationfilm 15. By thinning the thickness of the film of the second insulationfilm 15 than a height of the conductor pillar 14 to expose the top ofthe pillar 14, the surface can be planarized at the same time asremoving the exposed top of the conductor pillar 14 by using the CMPmethod etc. (FIG. 3A and FIG. 3B).

Next, the second wiring trench 16 of the same shape as the wiringpattern of the upper level wiring is formed on the surfaces of thesecond insulation film 15, for example, with the RIE method (FIG. 4A andFIG. 4B). When forming this trench, the trench is dug down to a depthbeing deeper than a depth to which at least a part of the conductorpillar 14 is exposed. Moreover, a step of cleaning the surface of theexposed conductor pillar 14 by using a CDE (Chemical Dry Etching)method, a wet etching method or a sputter-etching method with an inertgas etc. after forming the second wiring trench 16.

Next, an AlCu metal layer is formed on the second insulation film 15 andin the second wiring trench by using the sputtering method etc. The AlCualloy is used in this explanation, but Al, AlSiCu, and Cu, etc. can beused for the metal layer. The metal layers other than the parts of thesecond wiring trench 16 are removed by using the CMP method and the CDEmethod, etc. after forming the metal layer, and then the upper levelwiring 18 which is the second wiring is formed (not shown).

As described above, the problem of increasing contact resistance at thecontact hole bottom and an excessive etching at the missaligned regionsince it becomes unnecessary to perform a dry etching for the contacthole opening which has been used in the conventional method of formingthe contact hole according to the first embodiment. As a result, itbecomes possible to form the multi-level wiring structure having anexcellent electric characteristic and a high reliability.

The second embodiment will be s explained referring to FIG. 5A to FIG.6.

The second embodiment is characterized by forming a hard mask on anupper surface of a conductive pillar which becomes a connection plug andimproving the processing characteristics. FIG. 5A to FIG. 5J aremanufacturing step sectional views of the semiconductor device. FIG. 6shows a plan view of the manufacturing step sectional view shown in FIG.5J. A semiconductor substrate 10, for example, which consists of thesilicon semiconductor is shown in FIG. 5A and FIG. 5J, but is omitted inother figures.

First, a first insulation film 11, which consists of the silicon oxidefilm etc. formed by the CVD method etc., is formed on the semiconductorsubstrate 10. The surface of the first insulation film 11 is planarized,and the first wiring trench having the same shape as the wiring patternof the lower level wiring is formed on the surface. And, a metal, whichconsists of for example the AlCu alloy, is buried in this first wiringtrench, and then the lower level wiring 12, which is the first wiring,is formed (FIG. 5A). Next, the hard mask 131, which consists of siliconnitride film (Si₃N₄), is formed by using plasma CVD method etc. afterAlCu metal layer 13 is formed on the first insulation film 11 and thelower level wiring 12 by the sputtering method etc. (FIG. 5B). Next, aphotoresist (not shown) is patterned by using the photolithographymethod. The hard mask 131 of the silicon nitride film is patterned by,for example, the RIE method with the CF₄ faction gas system by usingthis photoresist as a mask, and the pattern is processed to a hard mask132 (FIG. 5C). Subsequently, the AlCu layer 13 is processed to theconductor pillar 14 which consists of the metal and has a pillar-shapedstructure by the RIE method using the Cl₂ gas system. The processingaccuracy to the pillar shape of a comparatively thicker AlCu layer canbe improved, as compared with the etching mask of the any photoresist,since the etching speed of the silicon nitride film to the Cl₂ factiongas is very small compared with the etching speed of AlCu (aluminumalloy). For example, in the pillar-shaped structure of 0.2 μm diameter,while the height, which can be manufactured when only the photoresist isused as the etching mask, is 4000 Å, a height more than 9000 Å can beachieved when a hard mask such as SiN is used.

A material used as the hard mask 131 may be a material which has a verylow etching speed compared with an etching speed of the metal layer 13during the etching of the metal layer 13, and is preferable to be ableto be removed easily by the CDE method and the wet etching method asdescribed later. For example, silicon oxide, silicon nitride, organicsiloxane, inorganic siloxane, tungsten, C, niobium or niobium nitride,etc. may be enumerated as a material of the hard mask 131. Where, sincethe protection effect of the pillar sidewall by the etching reactionproduct can be expected when the AlCu pillar is processed in a case thatthe organic siloxane film which includes C film and C and anotherorganic film voluminously are used as a hard mask, the processingaccuracy of the AlCu pillar can be improved. Al, AlSiCu, and Cu, etc.may be used as the metal layer 13 (FIG. 5D). Next, the second insulationfilm 15 such as the silicon oxide films is formed by the CVD method orthe spin coat method, etc. to bury the metal pillar 14 and the hard mask132. The step where this second insulation film 35 is formed may bedivided into several-steps, and a step of performing heat-treating etc.to perform the reforming of the insulation film may be added among them.The stacked structure of several kinds of different insulation films maybe used as this second insulation film 15 (FIG. 5E). Thus, the secondinsulation film 15 is etched-back by the CMP method to planarize thedifference after the second insulation film 15 is formed. At this time,the second insulation film 15 is etched-back until at least a part ofhard mask 132 is exposed.

In addition, the hard mask 132 partially exposed to the surface of thewafer consists of the silicon nitride film, and therefore, can be usedas an etching stopper at CMP of the second insulation film 15 such asthe silicon oxide films (FIG. SF). Next, the second wiring trench 16 isformed in the trench of the second insulation film 15 by the RIE methodetc. to expose a top portion of the metal pillar 14 from which the hardmask 132 is covered (FIG. 5G). Subsequently, the hard mask 132 isselectively removed from the second insulation film 15 and the metalpillar 14 by using the RIE method or the CDE method. A step of cleaningsurfaces of metal pillar 14 exposed in the second wiring trench 16 afterthis hard mask 132 is removed by using either of the CDE method, the wetetching method, the RIE method, and the sputter-etching method with theinert gas etc. may be added (FIG. 5H). Next, the AlCu metal layer 17 isformed on the second insulation film 15 and into the second wiringtrench 16 by using the sputtering method etc. (FIG. 5I).

Thereafter, the metal layer 17 other than inside the second wiringtrench is removed by using the CMP method etc., and the upper levelwiring 18, which is the second wiring, is formed (FIG. 5J and FIG. 6).

By using the second embodiment, it becomes unnecessary to perform thedry etching which has been used in the conventional formation method toopen the contact hole. Therefore, the problem of an increase of thecontact resistance at the bottom of the contact hole and an excessiveetching at the missaligned region, and it becomes possible to form themulti-level wiring structure with an excellent electric characteristicand a high reliability. Moreover, the processing of the pillar becomeseasy and the processing accuracy improves to use the hard mask when themetal pillar is processed. In addition, it becomes possible to increasean accuracy of planarity, since this hard mask can be used as an etchingstopper at a step of performing a CMP etch-back planarity of theinsulation film, which is the step thereafter.

The second wiring trench 16 may be formed to an upper portion of thesidewall of the metal pillar 14 (on the way of hard mask 132), though anetching is performed to expose the sidewall of the metal pillar 14 whenforming the second wiring trench 16 in the second above-mentionedembodiment. In this case, a structure when the hard mask is removed isshown in FIG. 7. FIG. 7 shows the same step to FIG. 5H. Other steps arethe same procedures shown in FIG. 5A to FIG. 5J.

As described above, the protection effect on an upper surface of thepillar during the process is achieved, and the allowance of thedifference of the depth of the second wiring trench 16 is enlarged byusing the hard mask 132. In addition, it functions as an absorptionlayer to the missalignment when the process shown in FIG. 8A to FIG. 8Dis used.

Therefore, it becomes possible to make the area on the upper surface ofthe pillar, which becomes electric contact surface, constant, even whenthe mask missalignment is caused between the upper wiring trench and theconnection plug, and the difference of an electric characteristic can bereduced.

The third embodiment will be explained referring to FIG. 9A to FIG. 9H.

FIG. 9A to FIG. 9H are manufacturing step sectional views ofsemiconductor device. The first interlevel insulation film 11, whichconsists of SiO₂ etc., is stacked on the semiconductor substrate 10 suchas silicon. The silicon oxide film (SiO₂) of the film thickness of 500nm by a spin-on method is used as the first interlevel insulation film11. Next, the first wiring trench 121 is formed by a photolithographyand an reactive ion etching (RIE). After the first wiring trench 121 isformed, PVD titanium nitride film 122 having about 5 nm thickness as abarrier metal, and PVD (physical vapor deposition) copper film 12 havingabout 800 nm thickness are deposited sequentially on the inner wall ofthe first wiring trench 121 (FIG. 9A). Next, a surplus part of titaniumnitride film 122 and PVD copper film 12 are removed by the CMP methodafter the semiconductor substrate 10 is heat-treated in order to promotethe Cu filling into the trench, and the lower level wiring 12 surroundedby the titanium nitride film 122 is formed into the first wiring trench121.

A method of depositing these materials is not especially limited andthese are deposited by the sputtering method, here. The semiconductorelement, the wiring, and the interlevel connection wiring, etc., whichhave already been formed under this wiring level, are omitted (FIG. 9B).The connection plug material is deposited on the first interlevelinsulation film 11 by the sputtering method in the order of a W/WN film(barrier layer) 123 and an Al film 14 (film for metal pillar) (FIG. 9C).This barrier layer 123 is used for the diffusion prevention of copper,and additionally, used as a stopper for the prevention of an excessiveetching when the metal pillar 14 is etched. In the present invention,the barrier layer 123 is not limited to this material. It is necessaryto make the barrier layer two layers so that the copper, which is thematerial of the lower level wiring 12 in this embodiment, is notdiffused when the lower level wiring 12 and the metal pillar 14 aredifferent metals in the embodiment, but the barrier layer may have onlyone layer in case of the homogeneous metal. In that case, the barrierlayer functions as a stopper for the excessive etching prevention whenthe metal pillar 14 is etched.

Next, the hard mask material 132 consisting of the silicon nitride film(Si₃N₄) is deposited on the connection plug material 123 and the metalpillar 14. After the photoresist 133 is coated on this hard maskmaterial 132, the photoresist 133 is patterned to the connection plugshape by the lithography. Thereafter, the hard mask material 132, themetal pillar 14, and the barrier layer 123 are etched by RIE by makingthe patterned photoresist 133 the mask, the barrier metal layer (W/WN)123 is arranged at lower portion, and then the metal pillar 14 coveredwith the hard mask 132 is formed. The CDE (Chemical Dry Etching) may beused only at the etching step of the W/WN film. A step of forming theconnection plug as mentioned above is an almost similar to the secondembodiment (FIG. 9D). Though barrier layer 123 is assumed to be W/WNhere, WN/W and W/WN/W, etc. can be further applied. Though a hard maskis used in the third embodiment (including embodiments thereafter), inthis embodiment, it is not always necessary. Therefore, though theembodiment, which uses a hard mask to give the allowance, is explainedin the later embodiments from the third embodiment, it is possible toapply also to the embodiment by which the formation of a hard mask isomitted.

Next, the protection film 19, which consists of the silicon nitride film(Si₃N₄), having a function of controlling the diffusion of the copperand controlling the oxidation of wiring is deposited by the CVD methodon the lower level wiring 12 (the first wiring) and metal pillar 14which has the barrier metal layer 122 under it (FIG. 9E). Followingthis, the second interlevel insulation film (SiO₂) 15 is deposited bythe CVD method to cover the metal pillar 14. At this time, the secondinterlevel insulation film 15 is deposited thicker than the metalpillars 14 to be able to form the trench for the second wiring at laterstep. And, the second interlevel insulation film 15 is planarized by theCMP (FIG. 9F). In FIG. 9E, the protection film 19 needs not be formed asa continuous film. For example, though details are described later,since the copper does not diffuse if the bottom of the metal pillar 14is covered so that the space between the metal pillar 14 and theprotection film 19 is not formed as shown in FIG. 10; the protectionfilm 19 may not be formed to the sidewall of the metal pillar 14 and theprotection film 19 at the sidewall of the metal pillar 14 may be thinnerthan the protection film 19 at the bottom even if the protection film 19is formed to the sidewall of the metal pillar 14. However, when thecopper is applied as a main material of the metal pillar 14, it isnecessary to form the protection film 19 having a proper thickness asfor the sidewall of the metal pillar 14.

Next, the second wiring trench 16 is formed in a usual method. At leasta part of the protection film 19 is exposed on the bottom of this wiringtrench (FIG. 9G). The protection film 19 exposed to the inner bottomsurface of the second wiring trench 16 formed in the second insulationfilm 15 and the hard mask 132 thereunder are etched and removed, atitanium nitride film (TiN) 135 of about 10 nm as a barrier layer isformed by using the PVD method, the copper film 17 is buried as a wiringmaterial and is used as the upper level wiring 17, and a surplus part ispolished by the CMP method and the interlevel insulation film 15 is madeflat (FIG. 9H).

Since the protection film which consists of the silicon nitride filmwith the Cu diffusion prevention effect and the oxidation control effectis deposited on the lower level wiring and the step of the contact holeopening in the interlevel insulation does not exist in order to formconnection plug by the above-mentioned method, an excellent connectioncan be obtained without requiring a complex process. In addition, theprotection film which consists of the silicon nitride film deposited onthe connection plug also has a function which enlarges the differenceallowance in the depth direction when the second wiring trench isprocessed with the hard mask described in the second embodiment.

The first modification of the third embodiment will be explained. In thethird embodiment, in the step of FIG. 9G and FIG. 9H, the protectionfilm 19 and the hard mask 132 are removed by the etching and the metalpillar 14 is exposed after the second wiring trench 16 is formed and theprotection film 19 is exposed.

In the first modification, the second interlevel insulation film 15 isplanarized to expose the protection film 19 for example by the CMPmethod as shown in FIG. 9F′. Thereafter, the third interlevel insulationfilm 15′ is deposited on the upper portion thereof, and the maskmaterial is formed on the third interlevel insulation film 15′. And, thesecond wiring trench 16 is formed, and the protection film 19 and thehard mask 132 are removed. Other processings are similar to the thirdembodiment. Therefore, the different material may be used to theinterlevel insulation films 15 and 15′ in this case. For example, SiO₂formed by the CVD or the spin-on method as the second interlevelinsulation film can be used. For example, stacking of the interlevelinsulation films having different permittivity becomes possibleaccording to the first modification.

The second modification of the third embodiment will be explainedreferring to FIG. 11A to FIG. 1C. As shown in FIG. 11A, after formingthe lower level wiring, the upper portion is removed by the etching.Thereafter, the barrier layer 123 (Hereinafter, called as a cap) isdeposited and to be a stopper layer (FIG. 11B). And, the surface is madeflat for example by the CMP method (FIG. 11C). Thereafter, since a stepof forming the pillar-shaped structure is similar to the thirdembodiment, an explanation will be omitted. Then, the second interlevelinsulation film 15 is formed without forming the protection film 19shown in the third embodiment in this case. Since the following stepsare the same as the third embodiments, the explanation will be omitted.In the second modification, the barrier layer 123 is used as a stopperlayer and the Cu is prevented from diffusion by preventing contactdirectly with an upper level without forming the protection layer 19.Therefore, it is unnecessary to form the protection film 19. This effectis as follows. The protection film 19 is basically formed with SiN.However, an operation speed becomes slow since SiN has a highpermittivity. However, it has an advantage that the operation speedbecomes fast compared with the third embodiment according to thismodification since there is no protection film 19.

The third modification of the third embodiment will be explained. Thethird modification is characterized in that a cap is provided like asthe second modification in the first modification. An advantage in thiscase is similar to the second modification.

The fourth embodiment will be explained referring to FIG. 12 to FIG.13F.

A step by which the metal pillar 14 is formed on the lower level wiring12 with a state of having formed the lower level wiring 12 on theinterlevel insulation film 11 on the semiconductor substrate 10 will beexplained referring to FIG. 12. There are various methods in the step bywhich the connection plug is formed to the pillar-shaped and the methodof using an electroless deposition will be described here.

The pattern which corresponds to the connection plug is formed on theinterlevel insulation film 11 by the photoresist. A copper layer isgrown by the electroless deposition in which a surface of the lowerlevel wiring 12 is used as a plating generation nucleus in the contacthole which becomes a connection plug. Thereafter, the pillar-shapedstructure of copper is formed as the metal pillar 14 when stripping offthe photoresist by the organic solvent. Then, the metal pillar 14 andthe interlevel insulation film 11 are coated by the protection film 19such as the silicon nitride films. In addition, the interlevelinsulation film 15 which consists of SiO₂ is formed by the spin-onmethod on the surface of the semiconductor substrate 10 and the trenchfor the upper level wiring is formed on the upper portion thereof. Thetitanium nitride film (TiN) 135 of about 10 nm is formed by using thePVD method to this wiring trench as a barrier layer, in addition, thecopper film 17 is buried as a wiring material, and a surplus part ispolished by the CMP method and is planarized.

A series of steps in which connections between the wirings are performedbased on the fourth embodiment is explained above. As known well, thecopper diffuses into the interlevel insulation film and causes theadverse effect to the device element. Then, it is necessary to cover allsurfaces of the copper by the diffusion control film (barrier layer) andthe protection film. However, all contact surfaces of the interlevelinsulation film 11 and the metal pillar 14 can not be covered with thestructure to pass the step shown in FIG. 12. This occurs remarkably whenan missalignment without alignment allowance is performed in thelithography step of the metal pillar 14 (part of 13 of FIG. 12). Then,in the substrate in which a practical step is passed, the copper leaksand diffuses in the part 13 because of the alignment shift (It is knownthat copper diffuses into the interlevel insulation film such as silicondioxide films by thermal and the electric field and causes deteriorationin the device characteristic, and it is important to cover with thediffusion control film).

Next, the manufacturing steps of the semiconductor device of the fourthembodiment will be explained referring to FIG. 13A to FIG. 13F. Thefirst interlevel insulation film 211 and the sacrifice film 212 whichconsist of SiO₂ etc. are stacked on the semiconductor substrate 200 suchas silicon one by one. The sacrifice film 212 may be a thin film whichconsists of the silicon nitride film. Here, the silicon oxide film(SiO₂) of 500 nm in the film thickness by the spin-on method is used asthe first interlevel insulation film 211. The silicon nitride film(Si₃N₄) of 20 nm in the film thickness with plasma CVD (Chemical VapourDeposition) is used as the sacrifice film 212. The sacrifice film usedin the present invention needs not be an insulation thin film, and, forexample, may be a conductive thin film such as the carbons. Next, thefirst wiring trench 213 is formed by the photolithography and theanisotropy etching (RIE: Reactive Ion Etching).

The sacrifice film 212 may be used as a mask material of the etching inthis step. That is, the sacrifice film 212 is processed by using thephotoresist pattern as a mask, and in addition the first interlevelinsulation film 211 is processed by using the sacrifice film 212 as amask. A flexibility of the etching condition used to process the firstinterlevel insulation film 211 is secured by this method. That is, thephotoresist may be transformed or disappeared during processing (FIG.13A). The PVD titanium nitride film 14 which is about 5 nm and the PVDcopper film 215 which is about 800 nm are deposited one by one on theinner wall of the first wiring trench 213 as a barrier metal to becomethe lower level wiring, after the first wiring trench 213 is formed, anda surplus part is polished and removed by the CMP. In addition, thetungsten film 216 is deposited on the surface of the copper by the CVDmethod in 5 nm as a protection film by the selective growth. When thelower level wiring 215 is aluminum, this film is unnecessary (FIG. 13B).

The photoresist 217 is formed on the first interlevel insulation film211 and the sacrifice film 212 where the copper film 215 which becomesthe lower level wiring arranged is buried, and the contact hole for theconnection plug is formed to the photoresist 217. The film thickness ofthe photoresist 217 is finally decided in consideration of the necessaryheight of the connection plug. The film thickness is assumed to be 800nm here.

Thereafter, the copper is plated by using the electroless depositionliquid which has the sulfuric acid copper to be a principal componentand uses formalin as a reducer. The electroless deposition is selectivefilm growth basically on the metal, it grows up to the metallic part(tungsten film 216) exposed to the bottom of the opening of thephotoresist 217, and the contact hole is buried by plating. Though thereis a case the copper is formed in an undesired region as a nucleus ofthe defect and dust, etc. on photoresist 217, the particle of thisundesired copper can be excluded by CMP and wet processing (FIG. 13C).

Next, the connection plug 218 is formed by plating the copper whichburies the contact hole when stripping off the photoresist 217 by theorganic solvent. In addition, the exposure part of the silicon nitridefilm which is the sacrifice film 212 is etched isotropically by the downstream etching. The cave 220 is formed under portion of the connectionplug 218 with this step. Under such a condition, the tungsten film 219is deposited in about 5 nm by the selective growth CVD on the wholeexposed connection plug 218, and is made to the protection film 219 usedas a control film of the Cu diffusion or an oxidation control film.Naturally, the protection film 219 is formed in the cave 220 (FIG. 13D).

In addition, the second interlevel insulation film 221 of the filmthickness of about 800 nm is formed with a spin-off method on the firstinterlevel insulation film 211 to bury the connection plug 218, and thethird interlevel insulation film 222 which consists of Si₃N₄ of filmthickness of about 20 nm thereon is formed with the plasma CVD method(FIG. 13E). When the connection plug which connects the upper levelwiring with the further upper level wiring than the upper level wiringis formed, the third interlevel insulation film 222 is used, andperforms the same functions as the sacrifice film 212 of FIG. 13A andFIG. 13B.

Next, the wiring trench for the upper level wiring on the upper portionof the interlevel insulation films 221 and 222 is formed. The titaniumnitride film (TiN) 224 of about 10 nm is formed in this wiring trench asa barrier layer by using the PVD method, in addition the upper levelwiring 223 which consists of the copper film is buried and formed as awiring material, and a surplus part is polished and removed by the CMPmethod. As described above, the protection film 219 is formed in thecave 220 (FIG. 13F). Hereinafter, usual steps are used until the deviceis formed.

An explanation of a series of steps as described above. Since the Cuused for the wiring material (especially, connection plug material) iscovered enough with the protection films such as the diffusion controlfilms and the oxidation control films, the adverse effect is nevercaused for the device by diffusing in the interlevel insulation film,and, it is controlled that Cu is oxidized.

Various materials used in this embodiment, the replacement by a propermaterial is possible as long as it does not deviate from the purpose ofthe present invention. Steps on the step of which the tungsten film 216where the selective growth is performed for example as a protection filmon the surface of the copper, etc may be omitted. In this case, thetungsten 219 can be also formed to be simultaneously extended on thesurface of the lower level wiring 215, when the selective tungsten 219formed on the surface of the connection plug 218 is formed. Theformation method is not limited to the selective growth CVD, a varietyof formation methods like a method in which a metal thin film is formedwith non-selection, thereafter causes the alloy reaction with copper,and is left only in the contact part with the copper, and methods inwhich the selective growth of the metal film is performed by theelectroless deposition, etc. are possible.

The copper film may be thoroughly formed with the PVD for example, andprocessed to the pillar-shape by the lithography and the anisotropyetching, though in the formation of the connection plug 218, the copperis formed by using the electroless deposition in which the photoresistmask is used in the third embodiment.

Next, the fifth embodiment will be explained referring to FIG. 14A, FIG.14B, and FIG. 15.

FIG. 14A and FIG. 14B are the manufacturing step sectional views of thefifth embodiment. FIG. 15 is a manufacturing step sectional view in acase that there is a difference in the depth direction of the wiringtrench but is not followed the fifth embodiment. The fifth embodimenthas the feature in using the thickness of stacking the silicon nitridefilms used for a protection film and a hard mask deposited on the uppersurface of the connection plug as depth processing allowance of thetrench processing for the second wiring performed thereafter, after theprotection film which consists of the silicon nitride film where thereare the Cu diffusion control effect and the oxidation control effect isdeposited on the connection plug.

The fifth embodiment is the same as the fourth embodiment until thesecond interlevel insulation film is formed (that is, it is the same asthe third embodiment to FIG. 9F).

The etching of the silicon oxide film (SiO₂) of the second interlevelinsulation film 319 is stopped at a position where the protection film318 of the silicon nitride film is exposed without etching to thesurface of connection plug 320 when the second interlevel insulationfilm 319 is etching-processed and the trench 321 for the second wiringis formed (FIG. 14A). Thereafter, the etching is advanced again in acondition of which an etching speed of the silicon nitride film is muchlarger than that of the silicon oxide film and the surface of connectionplug 320 is exposed (FIG. 14B). Thereafter, the upper level wiring(barrier layer 322 which consists of TaN and copper layer 323) which isthe second wiring is formed in this wiring trench 321. The depthdifference of the trench 321 for the second wiring in taken theabove-mentioned steps can be absorbed by the thickness of the siliconnitride films 316 and 318. In FIG. 15, since the second interlevelinsulation film 319 is etched to expose the pillar sidewall in a righttrench, it is drawn that the protection film of an upper portion of thepillar is left and the protection film at the sidewall of the pillar isremoved. However, a part of the protection film in the sidewall actuallyremains without being completely removed occasionally (followings aresame).

Next, the sixth embodiment will be explained referring to FIG. 16A andFIG. 16B.

FIG. 16A and FIG. 16B are sectional views of the semiconductor device.In the fifth embodiment, it is processed to the shape of the skirtextension (FIG. 16A) in the part of the vicinity of the joint section ora structure (FIG. 16B) of steps (part in barrier layer 416) in the lowerdirection which has extended for the coverage improvement of theprotection film 418 which consists of the silicon nitride film havingthe Cu diffusion control function or the oxidation control function inthe vicinity of the joint section with the lower level wiring 415 whichconsists of the connection plug 420 and the Cu. In any case, theprotection film 418 becomes possible to cover this part enough. That is,the coverage of the protection film 418 in the connection plug 420 andthe parts other than the contact section with the lower level wiring 415thereunder is improved and the reliability can be improved.

The barrier layer 416 has a shape of the skirt extension or a stepstructure in the sixth embodiment to improve the coverage. However, itis not limited to this, and a structure that the connection plug 420 isbroadened at the lower section, for example. In that case, a structuremay be a structure that the cross-section of the connection plug 420increases from the upper section to a lower section or may be astructure of the skirt extension.

Next, the seventh embodiment will be explained referring to FIG. 17A toFIG. 18.

FIG. 17A to FIG. 18 are sectional views of the semiconductor devicewhich has various shapes of the protection films. The protection film518 which consists of the silicon nitride film having the Cu diffusioncontrol function or the oxidation control function in the vicinity ofthe joint section with the lower level wiring 515 which consists of Cuhas the Cu diffusion control effect if the protection film 518 isdeposited on the interlevel insulation film 511 and the lower levelwiring 515 which consists of Cu. In this case, the Cu diffusion controleffect is irrespective of the manner of depositing the protection film518 of the connection plug 520. For example, in FIG. 17A, the protectionfilm is thinly deposited on the side of the connection plug 520, and isthickened thoroughly than other parts. If the protection film 518 isdeposited on the lower level wiring 515 and the near first interlevelinsulation film 511, a part of the protection film 518 deposited on thefirst interlevel insulation film 511 may be removed if necessary (FIG.17B). In FIG. 18, the protection film 518 is thinly deposited on theconnection plug 520, and thickly deposited on the interlevel insulationfilm 511. Thus, the method of forming the protection film 518 can bevariously modified, and if the diffusion prevention of the Cu can beperformed besides the deposition method of the seventh embodiment, theprotection film may be formed in any structure.

FIG. 19A to FIG. 19C are step sectional views which show themanufacturing method according to the eighth embodiment of the presentinvention. In the step chart shown in FIG. 19A to FIG. 19C, the elementisolation and the MOSFET, etc. are omitted, and a step according to thelogical arithmetic processing of generating the dummy pattern and theformation of multi-level metal wiring (a Double-Level-Metal: DLM) havingtwo layers.

First, the low permittivity film 620 is formed on the semiconductorsubstrate 600 such as the silicon substrate through the insulationisolation layer 610 as shown in FIG. 19A, and thereafter the metalwiring (lower level wiring 630) on the lower level side which consistsof the high melting point metal film 631 and the metal film 632 isformed. In the eighth embodiment, a case that the burial type Al-Cualloy metal wiring (Al-Cu Damascene) is used as the lower level wiring630 will be explained.

First, the low permittivity film 620 in which a ratio permittivity kvalue is 3.9 or less is formed on the semiconductor substrate 600through the insulation isolation layer 610. Some materials and theformation methods may be considered for this low permittivity film 620.For example, the low permittivity film 620 can be formed by forming thesilicon oxide film to which fluorine (F) or boron (B) is added by thelow pressure plasma CVD method. A silicate system film and the a polymersystem film formed with the spin-on method can be used. Both an organicsystem film which includes an organic component and an inorganic systemfilm which does not include an organic component can be used for asilicate system film. Additionally, the organic system film obtained bythe deposition polymerization method can be used. Since the insulationfilm in which a low permittivity is not necessary exists according tothe semiconductor device, the SiO₂ film by the CVD method generally usedand the BPSG and the PSG film, each of which contains boron (B) andphosphorus (P), etc. may be used for these insulation films. In theseventh embodiment, it is assumed the organic SOG film formed with thecoating method is used as a low permittivity film. In this case, afterthe organic SOG (spin-on glass) is coated in the film thickness of 0.5μm as the film thickness corresponding of the lower level wiring 630, aheat-treatment is performed at 450° C., and the organic SOG is stiffenedand is stabilized.

The trench is formed to the organic SOG film 620 with the lithographyand the RIE after above-mentioned organic SOG film 620 is formed, andthe metal material which becomes the lower level wiring is filled to thetrench. For example, after depositing the titanium nitride film 14 a(TiN film) of 10 nm which has a high melting point metal by the methodof sputtering, the Al-Cu alloy film 632 of 0.6 μm is deposited at 450°C. as this filling step. Thereafter, a surplus metal outside the trenchis removed by the chemical mechanical polishing (CMP), the surface isplanarized, and the lower level wiring 630 buried in the trench isformed. Thus, the structure shown in FIG. 19A is obtained.

Next, a step by which the pillar 640 and the interlevel insulation film650 are formed as shown in FIG. 19B is performed.

Though the pillar is formed only at portions which become the contactand via hole in the conventional art, it is enabled to avoid the problemof the resolution because the lithography of the hole pattern need notbe performed by forming the pillar. However, the pattern density of thecontact hole and the via hole in the semiconductor device and, in otherword, pattern density of the pillar are extremely small with less thanabout 5%, and the phenomenon that the low density pattern of the pillaris excessively etched by the step in which the pillar is processed tothe pillar-shaped after the lithography is occurred. When the interlevelinsulation film is deposited to planarize after the pillar is formed,the pattern dependency becomes large and the planarity characteristic isdeteriorated. Therefore, the planarity changes according to thedifference of a standard pattern density of the local regionstandardized at several hundreds μm region. That is, the problem thatthe film thickness of the interlevel insulation film becomes thick inthe part where a standard pattern density of the local region is high,and the film thickness of the interlevel insulation film thins in thepart where a standard pattern density of the local region is low occurs.Especially, when the interlevel insulation film is formed by using theformation technique of the coating (spin-on) type, this influence islarge.

Then, to solve such a problem, the dummy pattern which has asupplementary role of the manufacturing process is generated based onthe design information of the semiconductor device by the logicaloperation processing, and a standard pattern density at a local regionand the pattern density to the entire semiconductor device are increasedby arranging this dummy pattern, that is, the dummy pillar.

The following arithmetic processings are performed in this embodiment,though some methods are considered to the above-mentioned logicaloperation processing. FIG. 20 is an explanation chart which shows theflow of this arithmetic processing, and, hereinafter, this arithmeticprocessing will be explained referring to FIG. 20.

First, based on the wiring data of the upper level wiring (n wirings)and the lower level wiring (n−1 wirings), the logical operation of NOR(NOR) is processed to data of these two layers. A data D11 of a regionarranged neither the upper level wiring nor the lower level wiring isextracted by the arithmetic processing of the NOR. Next, the minusconversion difference (for example, ΔL=−1.0 μm) is added to theextracted regions, and, the obtained data as a result is assumed to beD12. Thus, the region which is apart from the boundary at 1 μm or morein the region where at least one of the upper level wiring and the lowerlevel wiring is arranged by providing the conversion difference of 1 μmfor instance for a region which corresponds to the data D11 isextracted. In this processing, a region which a shorter side is 2 μm orless at a previous stage where the minus conversion difference isperformed is deleted from the data D12. Next, an arithmetic processingin which a region corresponding to the data D12 is divided into anisland-shape and extracted is performed, and the obtained data as aresult is assumed to be D13. As for the division processing at thistime, it is preferable in the essential connection pattern design ruleused in this layer to divide into the united size. For example, theisland-shaped pattern is assumed to a square in which one side is 1 μm,and an interval of adjacent island-shaped pattern with each other isassumed to be 1 μm.

Next, the arithmetic processing of the OR (OR) of data D14 obtained by aNOT of data of the essential connection hole pattern and data D13obtained by the above-mentioned series of an arithmetic processing isperformed, and, the obtained data as a result is assumed to be finaldata D15.

The method by which a similar result is obtained is variously consideredconcerning the procedure of the above-mentioned arithmetic processing bythe logical conversion based on an exchange law (X+Y=Y+X, X·Y=Y·X),coupling law (X+(Y+Z)=(X+Y)+Z, X·(Y·Z)=(X·Y)·Z), distribution law(X+Y·Z=(X+Y)·(X+Z), X·(Y+Z)=X·Y+X·Z), absorption law(X·(X+Y)=X·X+X·Y=X), and de Morgan's theorem etc.

In the data D15 obtained as mentioned above, the pattern exists in bothregions of the hole pattern section for an essential connection and thedummy pattern section obtained by the logical operation, and the resistremains in these regions at lithography. Therefore, the density of thepattern in the whole area of the semiconductor device can be increased.For example, the pattern density is 19% for a certain microprocessor.

Return to an explanation of steps of FIG. 19B, for example, Al-Cu filmis deposited at a thickness (for example, 0.7 μm) larger than a depth ofthe via hole to the whole surface by the sputtering method.Subsequently, the pattern of the pillar is transferred to the resist byusing the mask manufactured based on the data obtained by the arithmeticprocessing and the pillar 640 of the Al-Cu film is formed with the RIEby using the resist mask to which the pattern is formed by thelithography technology. Thereafter, after the organic SOG which becomesthe interlevel insulation film 650 is coated at 1.1 μm thicknessequivalent to a film thickness of the upper level wiring, heat-treatingis performed at 450° C. and the organic SOG 650 is stiffened andstabilized.

Next, the interlevel insulation film 650 is planarized by using the CMPto remove the film thickness difference tuned to the arrangement of theground pillar material 11 generated on the surfaces of the interlevelinsulation film 650. Subsequently, the double level metal wiringstructure as shown in FIG. 19C is manufactured by forming the upperlevel wiring 17 of the burial type which consists of TiN film 661, whichis a refractory metal, and Al-Cu alloy film 662 similar to the formationof the lower level wiring 630 as previously explained.

The ninth embodiment of the present invention will be explainedreferring to FIG. 21 to FIG. 22A.

In the eighth embodiment, an example of leaving the formed pillar-shapedstructure (pillar) as it is and connecting the upper level wiringdirectly with this is shown. When the pillar-shaped structure can beremoved by the step thereafter, it is possible to simplify theprocessing of the logical operation of the dummy pattern generation morethan the technique explained in the eighth embodiment. FIG. 21 is anexplanation chart which shows the flow of this arithmetic processing,and, Hereinafter, an explanation will be made referring thereto.

First, the minus conversion difference (for example, ΔL=−1.0 μm) isadded to the hole data D21 which is a contact and/or a via hole whichbecomes a connection region of the upper level wiring (n wiring) and thelower level wiring (n−1 wiring), and, the obtained data as a result isassumed to be D22. In this case, the region apart from the boundary inthe region where the connection region of the upper level wiring and thelower level wiring is arranged at 1 μm or more by providing theconversion difference of 1 μm for instance for the region whichcorresponds to the data D21 is extracted. In this processing, a regionwhose shorter side is 2 μm or less at a previous stage where the minusconversion difference is performed is deleted from the data D22.

Next, an arithmetic processing in which a region corresponding to thedata D22 is divided into an island-shaped pattern and is extracted isperformed, and the obtained data as a result is assumed to be D23. Asfor the division processing at this time, it is preferable in theessential connection pattern design rule used in this layer to divideinto the united size. For example, the island-shaped pattern is assumedto a square in which one side is 1 μm, and an interval of adjacentisland-shaped pattern with each other is assumed to be 1 μm.

Next, the arithmetic processing of the OR (OR) of data D24 obtained by aNOT of data of the essential connection hole pattern and data D23obtained by the above-mentioned series of an arithmetic processing isperformed, and, the obtained data as a result is assumed to be finaldata D25.

In the data D25 obtained as mentioned above, the pattern exists in bothregions of the hole pattern section for an essential connection and thedummy pattern section obtained by the logical operation, and the resistremains in these regions at lithography. Therefore, the pattern densityin the whole area of the semiconductor device can be increased. Forexample, the pattern density is 42% for a certain microprocessor.

Hereinafter, a manufacturing method using the above-mentioned logicaloperation processing will be explained referring to the step sectionalviews shown in FIG. 22A to FIG. 22F. These step charts omit the elementisolation and MOSFET, etc., and mainly show the steps according to theprocessing of the logical operation of the dummy pattern generation andthe formation of multi-level metal wiring (a Double-Level-Metal: DLM)which consists of two layers.

As shown in FIG. 22A, similar to the eighth embodiment, the lowpermittivity film 620 is formed on the semiconductor substrate 600 ofthe silicon substrate etc. through the insulation isolation layer 610,and thereafter the buried metal wiring (lower level wiring 630) on alower side which consists of the refactory metal film 631 and the metalfilm 632 is formed.

Next, as shown in FIG. 22B, an SiO₂ film of 5 nm in thickness isdeposited by the low pressure plasma CVD method on the whole surface,subsequently, an HSQ (Hydrogen Silsesquioxane) 702 having the filmthickness more than the depth of the via hole is deposited, and an SiO₂703 of 10 nm in thickness is deposited by the low pressure plasma CVDmethod.

Next, the pattern is transferred to the resist by using the maskmanufactured based on the data obtained by the above-mentionedarithmetic processing by the lithography technology. As shown in FIG.22C, by using the formed resist pattern as a mask, the pillar 700 isformed by etching the stacking film which consists of the SiO₂ film 701,the HSQ film 702, and the SiO₂ 703 by the RIE technology.

Thereafter, as shown in FIG. 22D, after the organic SOG which becomesthe interlevel insulation film 710 is coated at 1.1 μm thicknessequivalent to a film thickness of the upper level wiring, heat-treatingis performed at 450° C. and the organic SOG 710 is stiffened andstabilized.

Next, the interlevel insulation film 710 is planarized by using the CMPto remove the film thickness difference tuned to the arrangement of theground pillar material 700 formed on the surfaces of the interlevelinsulation film 710. Thereafter, the resist pattern 720 to form anopening in the connection region of the lower level wiring and the upperlevel wiring is formed on the interlevel insulation film 710.Subsequently, this resist pattern 720 is used as a mask, and theinterlevel insulation film 710 and the pillar 700 thereunder areremoved. When the pillar 700 is removed, the SiO₂ film of upper portionis processed by the RIE using the gas, the HSQ film is removed by thediluted HF which is diluted to 1:100 or an alkali solvent, and a lowerSiO₂ film is processed by the RIE using the gas including fluorocarbon.The structure of FIG. 22E is obtained by this step.

Thereafter, the DLM structure shown in FIG. 22F is manufactured byforming the upper level wiring 730 of the burial type which consists ofTiN film 731 which is the high melting point metal and the Al-Cu alloyfilm 732.

In the eighth embodiment, by adopting the logical operation processingas previously explained, the pillar which becomes a dummy remains in theregion where the lower level wiring and the upper level wiring areformed except the connected section of the lower level wiring and theupper level wiring. Therefore, it is preferable to used a lowpermittivity insulator as the pillar.

The tenth embodiment of the present invention will be explainedreferring to FIG. 24 to FIG. 25F.

The ninth embodiment is an embodiment to process without generating thedummy pattern for the predetermined specific region. That is, the dummypattern is not generated to an undesirable region to form the dummypattern (dummy pillar) in the circuit performance and the chipcharacteristic. In this case, the dummy pattern may be not generated fora specific region of all levels, or the dummy pattern may be notgenerated for only a specific region of a specific level. For example,the following regions may be provided as an example of a specific regionwhere the dummy pattern is not generated like this.

First, the region where a sensitive circuit to the parasitic capacitycaused by the interlevel insulation film, etc. are formed may beprovided as a specific region. The region where the spare circuitsection, the redundancy circuit section, and the fuse section arrangedin the circuit section are formed may be provided. In addition, theregions where the region with which the terminal section (PAD section)for an external connection is formed and the dicing line section isprovided may be provided as a specific region.

Specifically, for example, the dummy pattern may be generated for theregion where the specific region is excluded from the dummy patternobtained by the eighth embodiment or the ninth embodiment.

FIG. 23 and FIG. 24 are figures which show the flow of the arithmeticprocessing when the dummy pattern is generated for the region where aspecific region is excluded from the dummy pattern obtained by the ninthembodiment. FIG. 23 shows an example for performing processing in whicha specific region is removed after performing processing of subtractingthe conversion difference ΔL, and FIG. 24 shows an example forperforming processing in which a specific region is removed to the dataobtained by the arithmetic processing shown in FIG. 21.

FIG. 25A to FIG. 25F are figures which show the step sectional viewswhen the DLM structure is manufactured based on the data obtained by thearithmetic processing shown in FIG. 23 or FIG. 24. Steps of FIG. 25A toFIG. 25F correspond to the steps of FIG. 22A to FIG. 22F according tothe ninth embodiment, respectively. Therefore, a detailed explanationfor each step is referred to the ninth embodiment, and only a feature ofthis embodiment will be explained here.

In this embodiment, a step in which a specific region is removed isperformed as already explained, and the step in which the specificregion is removed is performed in the step of FIG. 25C. That is, thepillar which becomes a dummy is not formed in a specific region S in thestep of FIG. 25C which differs from the ninth embodiment shown in FIG.22C. As a result, the pillar which becomes a dummy is not formed in thespecific region in the structure finally obtained as shown in FIG. 25F.

Some embodiments of the present invention are explained above, but thepresent invention is not limited to each of these embodiments and can becarried out by a variety of transforming it within the scope of thepresent invention.

Additional advantages and modifications will readily occur to thoseskilled in the art. Therefore, the present invention in its broaderaspects is not limited to the specific details, representative devices,and illustrated examples shown and described herein. Accordingly,various modifications may be made without departing from the spirit orscope of the general inventive concept as defined by the appended claimsand their equivalents.

What is claimed:
 1. A semiconductor device comprising: a semiconductorsubstrate in which a first insulating layer having a trench where alower level wiring is buried is formed; a conductive pillar-shapedstructure which is connected with said lower level wiring and formed onsaid semiconductor substrate, and wherein a thin film which becomes ahard mask on an upper portion thereof, and formed by using the hard maskas an etching mask; a second insulating layer formed on saidsemiconductor substrate to surround said pillar-shaped structure, saidsecond insulating layer having at least one trench which has a trenchformed by exposing at least said hard mask by selectively etching asurface of said second insulation layer, and being formed by removingsaid hard mask; an upper level wiring which is formed by being buried insaid trench, and is electrically connected with said pillar-shapedstructure; and a protection film formed on a surface of said lower levelwiring which is not covered with at least said pillar-shaped structure.2. The semiconductor device according to claim 1, said at least onetrench in said second insulation film is formed by removing saidprotection film on a surface of said pillar-shaped structure, after aprotection film is formed on a surface of said lower level wiring whichis not covered with at least said pillar-shaped structure.
 3. Asemiconductor device comprising: a semiconductor substrate in which afirst insulation layer having a trench where a lower level wiring isburied is formed; a conductive pillar-shaped structure which isconnected with said lower level wiring and formed on said semiconductorsubstrate; a second insulation layer formed on said semiconductorsubstrate to surround said pillar-shaped structure, said secondinsulating layer having a first trench having a same horizontal sectionshape as said pillar-shaped structure and a second trench which isformed on an upper portion of said first trench and has a horizontalcross-section larger than a cross-section in a horizontal section ofsaid pillar-shaped structure; an upper level wiring formed in said firsttrench and said second trench and electrically connected with saidpillar-shaped structure; and a protection film formed on a surface ofsaid lower level wiring which is not covered with at least saidpillar-shaped structure.
 4. A semiconductor device comprising: asemiconductor substrate in which a first insulation layer having atrench where a lower level wiring is buried; a conductive layer having acomponent, which includes a barrier metal function, formed in said lowerlevel wiring; a conductive pillar-shaped structure connected with saidconductive layer and formed on said semi-conductor substrate; a secondinsulation layer formed on said semi-conductor substrate to surroundsaid pillar-shaped structure, said second insulation layer having of atrench formed to expose an upper portion of said pillar-shapedstructure; and an upper level wiring formed in said trench andelectrically connected with said pillar-shaped structure.
 5. Thesemiconductor device according to claim 4, wherein said conductive layerhas at least two layers.
 6. The semiconductor device according to claim5, wherein said conductive layer has at least first and second layers,the first layer of said conductive layer functions as an etching stopperwhen said pillar-shaped structure is processed and a barrier layer, andthe second layer of said conductive layer has lower resistance than thefirst layer and functions as an etching stopper when said pillar-shapedstructure is processed.
 7. The semiconductor device according to claim4, wherein said conductive layer includes WN.
 8. The semiconductordevice according to claim 5, wherein said conductive layer includes W.9. The semiconductor device according to claim 4, wherein surfaces ofsaid lower level wiring and said first insulation layer is substantiallyin a same plane, said conductive layer is formed so as to be connectedwith at least a part of said lower level wiring, and said semiconductordevice further comprises a protection film coating a surface of saidlower level wiring which is not covered with at least said pillar-shapedstructure, and formed to deposit on an upper portion of saidpillar-shaped structure.
 10. The semiconductor device according to claim4, wherein said conductive layer is formed in said trench to cover allsurfaces of said lower level wiring.
 11. The semiconductor deviceaccording to claim 4, wherein said conductive layer includes materialwhich can be selectively etched to said first insulation film.
 12. Thesemiconductor device according to claim 4, wherein a horizontal sectionof said pillar-shaped structure is narrower than a horizontal section insaid conductive layer.
 13. The semiconductor device according to claim4, wherein said pillar-shaped structure or a conductive layer has ashape of widening toward an end.
 14. The semiconductor device accordingto claim 4, further comprising a protection film formed to cover asidewall of said pillar-shaped structure, said lower level wiring, andsaid first insulation layer.
 15. The semiconductor device according toclaim 4, wherein said lower level wiring includes copper or an alloythereof.
 16. The semiconductor device according to claim 4, wherein saidconductive layer is used as a CMP stopper when said lower level wiringis formed with the CMP.
 17. The semiconductor device according to claim16, wherein said lower level wiring includes copper or an alloy thereof.18. A semiconductor device comprising: a plurality of pillar-shapedstructures formed in a connection region where a lower level wiring andan upper level wiring are electrically connected; a plurality of dummypillar-shaped structures formed in a predetermined region except saidconnection region; and an interlevel insulation film formed to coversaid plurality of pillar-shaped structures, wherein a layout data ofsaid dummy pillar-shaped structure formed in said predetermined regionis obtained by a NOR processing of data which corresponds to bothinformation based on layout information of a layout of said lower levelwiring and layout information of a layout of said upper level wiring.19. The semiconductor device according to claim 18, wherein apillar-shaped structure formed in said connection region and saidpredetermined region is formed with a conductor.
 20. The semiconductordevice according to claim 18, wherein said dummy pillar-shaped structureformed in said predetermined region is formed in a region except apregiven specific region.
 21. A semiconductor device comprising: aplurality of pillar-shaped structures formed in a connection regionwhere a lower level wiring and an upper level wiring are electricallyconnected; a plurality of dummy pillar-shaped structures formed in apredetermined region except said connection region; and an interlevelinsulation film formed to cover said plurality of pillar-shapedstructures, wherein a layout data of a pillar-shaped structure formed insaid predetermined region is obtained by a NOT processing of data whichcorresponds to the information based on the layout information of alayout of said connection region.
 22. The semiconductor device accordingto claim 21, wherein the pillar-shaped structure formed in saidconnection region is removed after said interlevel insulation film isformed.
 23. The semiconductor device according to claim 21, wherein saiddummy pillar-shaped structure formed in said predetermined region isformed in regions except a pregiven specific region.
 24. Thesemiconductor device according to claim 22, wherein said dummypillar-shaped structure formed in said connection region and saidpredetermined region is formed with the insulator.
 25. A semiconductordevice comprising: a semiconductor substrate in which a first insulationlayer having a trench where a lower level wiring is buried is formed; aconductive pillar-shaped structure which is connected with said lowerlevel wiring and formed on said semiconductor substrate; a protectionfilm coating a surface of said lower level wiring which is not coveredwith at least said pillar-shaped structure, and formed to deposit on anupper portion of said pillar-shaped structure; a second insulation layerformed on said semiconductor substrate to surround said pillar-shapedstructure, said second insulation layer having at least one trench whichhas a trench formed by selectively etching and exposing at least anupper portion of said protection film and formed removing a part of atleast the upper portion of said protection film; and an upper levelwiring which is formed by being buried in said trench, and iselectrically connected with said pillar-shaped structure.
 26. Asemiconductor device comprising: a semiconductor substrate in which afirst insulation layer having a trench where a lower level wiring isburied is formed; a conductive pillar-shaped structure which isconnected with said lower level wiring and formed on said semiconductorsubstrate; a second insulation layer formed on said semiconductorsubstrate to surround said pillar-shaped structure, a third insulationlayer formed on said second insulation layer having a first trenchhaving the same horizontal section shape as said pillar-shaped structureand a second trench which is formed on an upper portion of said firsttrench and has a horizontal cross-section larger than a cross-section ina horizontal section of said pillar-shaped structure; an upper levelwiring formed in said first trench and said second trench andelectrically connected with said pillar-shaped structure; and aprotection film formed on a surface of said lower level wiring which isnot covered with at least said pillar-shaped structure.